sintering 
manufacturing


Named according

IEC 643

Thermal

Resistance

 °C

Bending Strength


MPa at 20°C

Thermal

Conductibility

W(mK)-1 at 20°C

Al2O3 > 99,7%

C799

1750

300

25

ZrO2

Partially Stabilised

C830

900

1200

2

ZrO2

Fully Stabilised

C830

2300

300

2

AlN

C910

1200

250

120

Y2O3


2200

100

9

MgO

C820

2200*

50

8

deutsch

The values depending on the shape, surface and the application conditions and are for reference only..Exact values have to be determined according to samples.

*The recommended application temperature is lower due to the high vapor pressure (Ca. 1650°C).